Abstract
A wide range of solid solution formation in the Li4GeO4-Li2ZnGeO4-Li3PO4 system was observed to occur with a structure based on γII-Li3PO4. This includes the fast Li conductor lisicon (Li14Zn(GeO4)4). The ionic conductivities of solid solutions in this systems are reported. Much of the solid solution range is structually metastable at