Magnetic properties of hydrothermally synthesized greigite (Fe3S4)- II. High- and low-temperature characteristics

Abstract

The magnetic behaviour of hydrothermally synthesized greigite was analysed in the temperature range from 4 K to 700 °C. Below room temperature, hysteresis parameters were determined as a function of temperature, with emphasis on the temperature range below 50 K. Saturation magnetization and initial susceptibility were studied above room temperature, along with X-ray diVraction analysis of material heated to various temperatures. The magnetic behaviour of synthetic greigite on heating is determined by chemical alteration rather than by magnetic unblocking. Heating in air yields more discriminative behaviour than heating in argon. When heated in air, the amount of oxygen available for reaction with greigite determines the products and magnetic behaviour. In systems open to contact with air, haematite is the final reaction product. When the contact with air is restricted, magnetite is the final reaction product. When air is excluded, pyrrhotite and magnetite are the final reaction products; the amount of magnetite formed is determined by the purity of the starting greigite and the degree of its surficial oxidation. The saturation magnetization of synthetic greigite is virtually independent of temperature from room temperature down to 4 K. The saturation remanent magnetization increases slowly by 20-30 per cent on cooling from room temperature to 4 K. A broad maximum is observed at ~10 K which may be diagnostic of greigite. The coercive and remanent coercive force both increase smoothly with decreasing temperature to 4 K. The coercive force increases from ~50 mT at room temperature to approximately 100-120 mT at 4 K, and the remanent coercive force increases from approximately 50-80 mT at room temperature to approximately 110-180 mT at 4 K.