Tunable plasmon resonances in anisotropic metal nanostructures

Abstract

Coherent oscillations of free electrons in a metal, localized in a small volume or at an interface between a metal and a dielectric medium, have attracted a lot of attention in the past decades. These so-called surface plasmons have special optical properties that can be used in many applications ranging from optoelectronics to sensing of small quantities of molecules. One of the key issues is that electromagnetic energy can be confined to a relatively small volume close to the metal surface. This field enhancement and the resonance frequency strongly depend on the shape and size of the metal structures. In this thesis, several fabrication methods to create these metal structures on the nanometer to micrometer scale are presented. The optical properties are studied with a special emphasis on the effect of shape anisotropy. Self-assembled 2D colloidal crystals are used as mask to fabricate arrays of metal triangles on a substrate. One of the limitations of this nanosphere lithography technique is that the size of the holes in the colloidal mask (through which the metal is evaporated) is determined by the size of the colloids in the mask. The masks, however, can be modified by use of MeV ion beams and/or wet-chemical growth of a thin layer of silica, resulting in a reduced hole size. Arbitrary symmetry and spacing can be obtained by use of optical tweezers and angle-resolved metal deposition. In contrast to pure metals, amorphous materials like silica are known to show anisotropic plastic deformation at constant volume when subject to MeV ion irradiation. Gold cores embedded in a silica matrix, however, show an elongation along the direction of the ion beam, whereas silver cores rather disintegrate. Silver nanocrystals in an ion-exchanged soda-lime glass redistribute themselves in arrays along the ion beam direction. The optical extinction becomes polarization-dependent, with red- and blue-shifts of the plasmon resonances for polarizations longitudinal and transverse to the arrays, respectively. The band splitting is attributed to near-field electromagnetic plasmon coupling within the arrays. Finite difference time domain simulations indicate that the combination of particle center-to-center spacing and diameter, rather than inter-particle spacing alone, is the key parameter determining the coupling strength. The resonant electric field is concentrated in the very small gaps between the particles in the array. With the MeV ion beam technique, it is possible to fabricate large substrates with relatively monodisperse oblate ellipsoidal silica-core/metal-shell colloids, with the short axis aligned in the direction of the ion beam. The optical extinction of these particles, is a complex function of the core radius and the shell thickness, due to a competition between phase retardation effects and the coupling between the surface plasmons at the inner and outer surfaces of the shell. After deformation, the extinction is angle- and polarization-dependent. Calculations indicate that large Au-shell particles can sustain cavity modes, for which the electric field is enhanced in almost the full volume of the dielectric core. The resonance frequency is sensitive to the size, shape and dielectric constant of the core, and the polarization direction.